Ti3SiC2-PbO-Ag composites (TSC-PA) were successfully prepared using the spark plasma sintering (SPS) technique. The ingredient and morphology of the as-synthesized composites were elaborately investigated. The tribological properties of the TSC-PA pin sliding against Inconel 718 alloys disk at room temperature (RT) to 800 ◦C were examined in air. The wear mechanisms were argued elaborately. The results showed that the TSC-PA was mainly composed of Ti3SiC2, Pb, and Ag. The average friction coefficient of TSC-PA gradually decreased from 0.72 (RT) to 0.3 (800 ◦C), with the temperature increasing from RT to 800 ◦C. The wear rate of TSC-PA showed a decreasing trend, with the temperature rising from RT to 800 ◦C. The wear rate of Inconel 718 exhibited positive wear at RT and negative wear at elevated temperatures. The tribological property of TSC-PA was related to the tribo-chemistry, and the abrasive and adhesive wear.